Specifications
1)EVA film low shrinkage
2)Useful life>15years
3)High light transmittance >92.1%
4)VE EN take partly of PVB film
0.38mm,0.4mm and 0.76mm EVA Laminated film for Glass
1)EVA film low shrinkage
2)Useful life>15years
3)High light transmittance >92.1%
4)VE EN take partly of PVB film
Introduction
EVA Film for Laminated Glass
The latest VE/EN interlayer film is specially R&D by our own formula, which is most advanced at home and abroad. VE film with excellent transparence, adhesion, weather resistance, and tensile strength, The useful life can up to 15years with no de-lamination and cracks. It has passed the China National Safety Lamianted Glass Standard(GB9962-1999) and insuranced by PICC. VE film can successfully take partly of PVB to applied in outdoor by the advantage of outstanding properties.
Application
Outdoor architecturall; Curtain Wall; Automobile glasses; Bullet-proof glasses; skylight; doors and windows and other outdoor decorations etc.
Porperties
Useful life>15years
Based on the particular core technology, VE film has excellent weather-resistance, can absorb 99% UV ray radiation , can be applied in outdoor long-time with no de-lamination and cracks.
High light transmittance >92.1%
Adopt DuPon EVA resin materials and differentiation technique, make the film reach different transparence at different temperature, which can meet customer's specific demands.
Following processing data for reference.
Initial temperature | 60c15mins | remark |
Processing temperature | 120C-125C | 125C-135C | 135C-150C |
holding time | 70"-60" | 60"-45" | 45"-30" |
light transmittance rate | 90.1%-90.6% | 90.6%-91.5% | 91.5%-92.1% |
PRODUCT TECHNICAL PARAMETERS |
|
Test Item | Method | smart-PD | architectural | architectural | indoor high transparent | ordinary transparent |
-EN | EN-B |
Tensile strength | E&N LAB METHO | 6.4MPA | 8.1MPA | 6.4MPA |
|
|
Adhesion with glass | E&N LAB METHO | 95.7N/cm (180 peeling) | 99.7N/cm (180? peeling) | 94.6N/cm(180 peeling) |
|
|
Adhesion with organic polymer film | E&N LAB METHO | 17.8N/cm (180? peeling) | 21.3N/cm (180? peeling) | 15.4N/cm(180? peeling) |
|
|
High transmittance | E&N LAB METHO | =91.0% | =90.5% | =90.9% | =90.1% | =82.3% |
Haze | E&N LAB METHO | 0.29% | 0.47% | 0.50% | 0.69% | 3.23% |
UV block rate | E&N LAB METHO | 100% | 99% | 99% | 65% | 40% |
Elongation | ASTMD638 | 880% | 800% | 880% |
|
|
Shrinkage | E&N LAB METHO | =5% | =5% | =5% |
|
|
Water absorptioin | E&N LAB METHO | =0.01% | =0.01% | =0.01% |
|
|
Heat resistance | GB-15763.3 | No bubbles and degumming |
|
|
|
|
100?water for 2hrs | -2009 | No bubbles and degumming | No bubbles and degumming |
Humidity resistance | E&N LAB METHO | No bubbles and haze |
|
|
|
|
(60?,95%RH |
|
|
|
|
400hrs | No bubbles and haze | No bubbles and haze | No bubbles and haze | No bubbles and haze |
Anti-aging(radiation for 3000hrs) | E&N LAB METHO | light change<3%,no yellow change | light change<3%,no yellow change | light change<3%,no yellow change |
|
|
Cold and Heat shock(Cold-40?30mins,Heat80?30mins; 50circles) | E&N LAB METHO | No bubbles and degumming | No bubbles and degumming | No bubbles and degumming |
|
|
Impact resistance against shot bag | GB-15763.3-2009 | Qualified | Qualified | Qualified |
|
|
Ball impact peeling resistance | GB-15763.3- | Qualified | Qualified | Qualified |
|
|
2009 |
useful life | E&N LAB METHO | =20years | =15years | =15years |
|
|
|